Laser Welding Aluminium Alloy 5083

This results in shallow welds with a low aspect ratio.

Laser welding aluminium alloy 5083.

Full penetration butt welds of 2mm and 3mm gauge aa5083 using this process have been produced. Laser welding of aluminium alloy 5083 p okon g dearden k watkins m sharp p french laser group department of engineering university of liverpool brownlow street liverpool l69 3gh united kingdom lairdside laser engineering centre birkenhead wirral united kingdom abstract there are two laser welding mechanisms keyhole mode and conduction mode. The influence of experimental variables as the laser power and the linear welding rate on the sizes and properties of the butt weld beads has been studied. Typical fusion zone configuration of aa5083 aluminum alloy welded using 4 kw laser power and 6 m min welding speed at two different defocusing distancesisshown in figure 8.

In this work high power co2 and yag lasers have been used to produce laser conduction welds on 2mm and 3mm gauge aa5083 respectively by means of defocused beams. Conduction welds are usually produced using low power focused laser beams. Aa5083 and aa6013 are welded by the tungsten inert gas welding method with two different electrodes alsi12 alsi5 and six different sample parameters have been obtained as 5083 alsi12 5083. The material for experimental welding was non heat treatable wrought aluminum alloy 5083 o o designates annealed state heat treatment method of thickness of 5 mm.